Japanese Industrial Standards Data – Aluminum alloy die casting

A chart listing aluminum alloys for die-casting standardized by the Japanese Industrial Standards.

MENU

Japanese Industrial Standards

JIS H 5302 : 2006

Aluminum alloy die casting

Preface

The chart below is from the Japanese Industrial Standards and is based on the information contained in ISO/FDIS 3522: Aluminium and aluminium alloys-Castings-Chemical composition and mechanical properties published in 2006.

Table 2 – Chemical Composition 
Unit: Chemical composition (mass %)
Cu Si Mg Zn Fe Mn Cr Ni Sn Pb Ti Al
ADC1 1.0 max. 11.0 to 13.0 0.3 max. 0.5 max. 1.3 max. 0.3 max. 0.5 max. 0.1 max. 0.20 max. 0.30 max. Remainder
ADC3new window 0.6 max. 9.0 to 11.0 0.4 to 0.6 0.5 max. 1.3 max. 0.3 max. 0.5 max. 0.1 max. 0.15 max. 0.30 max. Remainder
ADC5 0.2 max. 0.3 max. 4.0 to 8.5 0.1 max. 1.8 max. 0.3 max. 0.1 max. 0.1 max. 0.10 max. 0.20 max. Remainder
ADC6 0.1 max. 1.0 max. 2.5 to 4.0 0.4 max. 0.8 max. 0.4 to 0.6 0.1 max. 0.1 max. 0.10 max. 0.20 max. Remainder
ADC10 2.0 to 4.0 7.5 to 9.5 0.3 max. 1.0 max. 1.3 max. 0.5 max. 0.5 max. 0.2 max. 0.2 max. 0.30 max. Remainder
ADC10Z 2.0 to 4.0 7.5 to 9.5 0.3 max. 3.0 max. 1.3 max. 0.5 max. 0.5 max. 0.2 max. 0.2 max. 0.30 max. Remainder
ADC12new window 1.5 to 3.5 9.6 to 12.0 0.3 max. 1.0 max. 1.3 max. 0.5 max. 0.5 max. 0.2 max. 0.2 max. 0.30 max. Remainder
ADC12Z 1.5 to 3.5 9.6 to 12.0 0.3 max. 3.0 max. 1.3 max. 0.5 max. 0.5 max. 0.2 max. 0.2 max. 0.30 max. Remainder
ADC14 4.0 to 5.0 16.0 to 18.0 0.45 to 0.65 1.5 max. 1.3 max. 0.5 max. 0.3 max. 0.3 max. 0.2 max. 0.30 max. Remainder
Al Si9(1) 0.10 max. 8.0 to 11.0 0.10 max. 0.15 max. 0.65 max. 0.50 max. 0.05 max. 0.05 max. 0.05 max. 0.15 max. Remainder
Al Si12(Fe)(2) 0.10 max. 10.5 to 13.5 0.10 max. 0.15 max. 1.0 max. 0.55 max. 0.15 max. Remainder
Al Si10Mg(Fe)(1) 0.10 max. 9.0 to 11.0 0.20 to 0.50 0.15 max. 1.0 max. 0.55 max. 0.15 max. 0.05 max. 0.15 max. 0.20 max. Remainder
Al Si8Cu3(2) 2.0 to 3.5 7.5 to 9.5 0.05 to 0.55 1.2 max. 0.8 max. 0.15 to 0.65 0.35 max. 0.15 max. 0.25 max. 0.25 max. Remainder
Al Si9Cu3(Fe)(2) 2.0 to 4.0 8.0 to 11.0 0.05 to 0.55 1.2 max. 1.3 max. 0.55 max. 0.15 max. 0.55 max. 0.25 max. 0.35 max. 0.25 max. Remainder
Al Si9Cu3(Fe)(Zn)(2) 2.0 to 4.0 8.0 to 11.0 0.05 to 0.55 3.0 max. 1.3 max. 0.55 max. 0.15 max. 0.55 max. 0.25 max. 0.35 max. 0.25 max. Remainder
Al Si11Cu2(Fe)(2) 1.5 to 2.5 10.0 to 12.0 0.30 max. 1.7 max. 1.1 max. 0.55 max. 0.15 max. 0.45 max. 0.25 max. 0.25 max. 0.25 max. Remainder
Al Si11Cu3(Fe) 1.5 to 3.5 9.6 to 12.0 0.35 max. 1.7 max. 1.3 max. 0.60 max. 0.45 max. 0.25 max. 0.25 max. 0.25 max. Remainder
Al Si12Cu1(Fe)(2) 0.7 to 1.2 10.5 to 13.5 0.35 max. 0.55 max. 1.3 max. 0.55 max. 0.10 max. 0.30 max. 0.10 max. 0.20 max. 0.20 max. Remainder
Al Si17Cu4Mg 4.0 to 5.0 16.0 to 18.0 0.45 to 0.65 1.5 max. 1.3 max. 0.50 max. 0.3 max. 0.3 max. Remainder
Al Mg9(1) 0.10 max. 2.5 max. 8.0 to 10.5 0.25 max. 1.0 max. 0.55 max. 0.10 max. 0.10 max. 0.10 max. 0.20 max. Remainder

Notes(1) Chemical components other than those given in the above table, including those shown in the table with “—” i.e., no specification values, shall be 0.05% max. for individual elements and 0.15% in total.

   (2) Chemical components other than those given in the above table, including those shown in the table with “—” i.e., no specification values, shall be 0.05% max. for individual elements and 0.25% in total.

Comparison table between JIS and related foreign standards (with material symbol)  
Standard Japanese Industrial Standard Related Foreign Standards
U.S.A U.K Germany France International Standard
JIS ASTM BS DIN NF ISO
Standard Number H2118:06 B179:03 EN1676:97 EN1676:97 EN1676:97
Standard Name Aluminum alloy ingot for die casting All casting aluminum alloy ingots Aluminum alloy ingot  
Material Symbol AD1.1 A413.1  
AD1.2 A413.2  
AD3.1 A360.1  
AD3.2 A360.2  
AD5.1  
AD5.2  
AD6.1  
AD6.2  
AD10.1 A380.1  
AD10.2 A380.2  
AD10Z.1  
AD12.1  
AD12.2 383.2  
AD12Z.1 383.1  
AD14.1 B390.1  
AD14.2 390.2  